Fiber glass reinforced phenolic moulding compound ZY6620

Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass,high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.

online service

Tel:0086-577-66608881/65060000

Email: lench@lench.net

Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass,high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.


We will keep learning, practicing, developing, we want to work for you like a team and strong enough to follow you.


Data Sheet

Model

ZY6620

Density

1.79g/cm3

Flexural strength

220MPA

Disc flow

17CM

Impact strength

12KJ/M2

Volume Resistance

1.0×1013Ω.cm

Distortion temperature

270℃

Shrinking rate

0.1%

Water absorption

0.1%

Flame test

V-0 UL94

Electric strength

14kv/mm


Moulding Condition

Moulding type

Compression

Preheating temperature

90-110℃

Preheating time

120-240S

Moulding temperature

160-190℃

Up mould temperature

170℃

Down mould temperature

160℃

Compression pressure

20-30MPA

Pressure keeping time

120-240S

Compressing speed

5-20S


After Curing Condition

150℃

180℃

210℃

230℃

2hours

6hours

8hours

3hours


Printing, Packaging,Transportation, Storage

Printing

The products must print the description, batch no. net weight, produce date, manufacturer, standard.

Package

25kg/bag. Anti-water bag.

Transportation

It is non-dangerous products.Transportation should avoid moisture, heat, dirt and packaging damage.

Storage

ZY series should be stored in a cool, dry, ventilated warehouse, room temperature should not exceed 35 ℃, not near to  the fire, heat or direct in sunlight. From the date of manufacture, storage period is 12 months.



 

Welcome to our website! Please send your words at any time in the following form and ask us, we will contact you and provide you with the corresponding service as soon as possible. Please write in English.

Fiber glass reinforced phenolic moulding compound ZY5010

Learn More

FIber glass reinforced phenolic moulding compound ZY7010

Learn More

Fiber glass reinforced phenolic moulding compound ZY3045

Learn More

Fiber glass reinforced phenolic moulding compound ZY6620

Learn More