FIber glass reinforced phenolic moulding compound ZY7010
Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass，high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.
online service
Tel:0086-577-66608881/65060000
Email: lench@lench.net
Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass，high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.
We will keep learning, practicing, developing, we want to work for you like a team and strong enough to follow you.
Data Sheet
|
Model |
ZY7010 |
|
Density |
1.74g/cm3 |
|
Flexural strength |
200MPA |
|
Disc flow |
60CM |
|
Impact strength |
10KJ/M2 |
|
Volume Resistance |
1.0×1014Ω.cm |
|
Distortion temperature |
270℃ |
|
Shrinking rate |
0.1% |
|
Water absorption |
0.1% |
|
Flame test |
V-0 UL94 |
|
Electric strength |
12kv/mm |
Moulding Condition
|
Moulding type |
Injection |
|
Moulding temperature |
160-190℃ |
|
preheating bottle head temperature |
65-75℃ |
|
preheating bottle back temperature |
30-60℃ |
|
Injection speed |
35-65RPM |
|
Injection Pressure |
90-140MPA |
|
Injection time |
10~20S |
|
Pressure keeping time |
5~15S |
|
Curing time |
30~60S |
After Curing Condition
|
120℃ |
150℃ |
180℃ |
200℃ |
|
2hours |
2hours |
2hours |
4hours |
Printing, Packaging,Transportation, Storage
Printing
The products must print the description, batch no. net weight, produce date, manufacturer, standard.
Package
Transportation
It is non-dangerous products.Transportation should avoid moisture, heat, dirt and packaging damage.
Storage
ZY series should be stored in a cool, dry, ventilated warehouse, room temperature should not exceed 35 ℃, not near to the fire, heat or direct in sunlight. From the date of manufacture, storage period is 12 months.
Welcome to our website! Please send your words at any time in the following form and ask us, we will contact you and provide you with the corresponding service as soon as possible. Please write in English.
Fiber glass reinforced phenolic moulding compound ZY5010
Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass，high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.
Learn More
FIber glass reinforced phenolic moulding compound ZY7010
Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass，high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.
Learn More
Fiber glass reinforced phenolic moulding compound ZY6620
Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass，high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.
Learn More
Fiber glass reinforced phenolic moulding compound ZY6010
Fiber glass reinforced phenolic moulding compound, it is different from the common bakelite, our compound contain 30-50% fiber glass，high tension strength and high temperature resistance, it is for making the insulation plastic parts for commutators, solenoid switch, brush holder and so on. It is widely used to automobile industries.
Learn More